Abstract: The proper choice of raw materials and manufacturing parameters for Cross Laminated Timber is essential to promote the proper bonding of the lamellas, aiming at their application in construction. However, few Brazilian species are currently used in the production of Cross Laminated Timber. The aim of this work was to characterize the bonding quality of four Brazilian reforestation species (Pinus elliottii (pino ellioti), Eucalyptus grandis (eucalipto), Toona ciliata (toona) and Acrocarpus fraxinifolius (lazcar)) in the manufacture of Cross Laminated Timber with two-component polyurethane adhesive and five different pressure levels (from 0,1 MPa to 1,3 MPa). Bonding quality was evaluated through delamination and glue line shear tests based on the European standard. Delamination was affected by the wood species, and the best adhesion occurred for the Cross Laminated Timber manufactured with Pinus elliottii (pino ellioti) and Acrocarpus fraxinifolius (lazcar) at the bonding pressure of 0,7 MPa. Cross Laminated Timber bonding pressure did not affect the percentage of wood in the shear test fractured surface, whereas higher density Cross Laminated Timber showed higher percentages.

Abstract: Oriented Strand Board is a structural wood composite with applications that require good physical and mechanical performance. The addition of ZnO nanoparticles is an alternative that has been studied in order to improve the properties of Oriented Strand Board panels. However, there is no information about its effect Oriented Strand Board. The aim of this work was to evaluate the influence of the addition of zinc oxide nanoparticles in two different percentages (0,25 % and 0,50 %) on the physical-mechanical properties of Oriented Strand Board panels produced with phenol-formaldehyde resin and on the heat transfer during hot-pressing. Oriented Strand Board panels were produced and tested according to European Standards. The addition of ZnO nanoparticles improved the dimensional stability of the panel, reducing its thickness swelling, and also increased the screw withdraw strength. The heat transfer during hot-pressing increased the temperature more quickly on boards with nanoparticles addition; on the other hand the final temperature of the control treatment was higher.

Abstract The Brazilian Code ABNT NBR 7190 (1997) is currently under review process and one of the proposals is the change and add of some test procedures. Several specimen geometric configurations and test conditions have been evaluated by the study committee CE-02:126.10. The aim of this paper was the analysis of the tensile strength perpendicular to the grain through the current Brazilian Code and from an adaptation of ISO 13910 (2005). Pine and Indian Cedar were used and simplified relationships were proposed. Numerical simulations were performed to identify the stress distributions in the specimens. The results obtained by ISO 13910 (2005) did not differ statistically for the two species. Brazilian standard method cedar had a higher strength value than pine. The simplified ratios obtained ranged between 0,017 and 0,123. The numerical simulations of ISO 13910 (2005) specimens showed predominant failure by tension in the lower fiber due to stress concentration.